一、产品介绍 I. Product Introduction |
|||||||
镁铁尖晶石砖是由镁砂和铁铝尖晶石为主要原料,高温烧结而成。 Ferrospinel brick is made from magnesite and Ferrospinel as main material under high temperature sintering. |
|||||||
其特点有:1、挂窑皮性能良,抗热热震稳定性良,窑皮形成迅速而稳定,不易剥落,筒体温度低。2、抗化学浸蚀性能优,抗过热性损毁性能优,抗氧化还原性能好,没有碱裂、疏松现象。3、特别是高温机械柔韧性优,耐磨损性能好,尤其是在回转窑的轮垫处它是最佳选择。4、适用性广,可在烧成带和过渡带同时使用它,会减少备用库存,降低成本。 Its characteristics: 1. Good clinker coating performance, anti-thermal shock stability. As the coating forms quickly and not easy to fall off, which ensure low kiln body temperature; 2. It is good in anti-chemical erosion, thermal damage and anti-oxidation reduction property. There is no alkali breakdown or loosing; 3. It is especially good at high temperature mechanical flexibility, anti-friction resistance, particularly for roller cushion of the rotary kiln; 4. For its wide range application, it can be used both at the burning zone and transition zone, which reduce the store and thus save cost. |
二、产品指标 II. Product Index |
||||||||||
奥鞍牌号 MRL BRAND |
MgO |
Al2O3 Fe2O3 |
显气孔率A.P |
体积密度B.D |
常温耐压C.C.S |
荷重软化R.U.L |
热震稳定性T.S.R |
热膨胀率T.E |
热导率T.C |
|
% |
% |
(%): |
(g/cm3) |
(Mpa) |
(Ta)℃ |
950℃风冷/次≥ |
1000℃% |
950℃(W/Mk) |
||
CFS-15A |
保证值 |
80.00 |
13~16 |
17.00 |
2.95 |
55.00 |
1680 |
100 |
1.15 |
2.60 |
典型值 |
83.67 |
13.78 |
16.41 |
2.97 |
98.00 |
>1680 |
>100 |
1.10 |
2.30 |
|
CFS-15B |
保证值 |
78.00 |
13~16 |
18.00 |
2.92 |
50.00 |
1660 |
90 |
1.15 |
2.60 |
典型值 |
81.86 |
13.55 |
17.22 |
2.94 |
85.00 |
>1660 |
>90 |
1.10 |
2.30 |
|
三、使用客户 III. Current customer |