一、产品介绍 I. Product Introduction |
|
硅莫砖是由高铝刚玉和碳化硅为主要原料,中温烧结而成的。 Alumisic was mainly made from high aluminum containing corundum and Silicon Carbide under medium temperature sintering. |
|
1、具有抗热震稳定性和热负荷疲劳性能优、高温机械柔韧性特优、耐磨性能特优、抗还原气氛性能特优等特点。2、导热系数低,降低了窑的筒体温度,防止回转窑筒体和托轮受热膨胀,隔热效果优,节能效果好。3、体积密度小,有效降低了窑筒体、托轮和动力系统的负荷。 1. It has many properties such as good thermal shock stability, good heat load fatigue, excellent high temperature mechanical flexibility, abrasion resistance, anti oxidation reduction; 2. its low heat conductivity can reduce the kiln proper temperature, prevent the rotary kiln and support roller from expansion, with good heat insulation and energy saving performance; 3. Its low bulk density can effectively reduce the load on kiln proper, support roller as well as driving system. 硅莫砖是最近几年在中国迅速推广的在过渡带使用的新产品,在大多数时候它的使用效果都比镁尖晶石砖好。 Alumisic brick is a new product used recently on the transition zone, which has been promoted in China. Its performance is better than that of Mag-spinel brick for most of the time. |
|
二、产品指标 II. product index |
一、产品介绍 I. Product Introduction |
|
硅莫砖是由高铝刚玉和碳化硅为主要原料,中温烧结而成的。 Alumisic was mainly made from high aluminum containing corundum and Silicon Carbide under medium temperature sintering. |
|
1、具有抗热震稳定性和热负荷疲劳性能优、高温机械柔韧性特优、耐磨性能特优、抗还原气氛性能特优等特点。2、导热系数低,降低了窑的筒体温度,防止回转窑筒体和托轮受热膨胀,隔热效果优,节能效果好。3、体积密度小,有效降低了窑筒体、托轮和动力系统的负荷。 1. It has many properties such as good thermal shock stability, good heat load fatigue, excellent high temperature mechanical flexibility, abrasion resistance, anti oxidation reduction; 2. its low heat conductivity can reduce the kiln proper temperature, prevent the rotary kiln and support roller from expansion, with good heat insulation and energy saving performance; 3. Its low bulk density can effectively reduce the load on kiln proper, support roller as well as driving system. 硅莫砖是最近几年在中国迅速推广的在过渡带使用的新产品,在大多数时候它的使用效果都比镁尖晶石砖好。 Alumisic brick is a new product used recently on the transition zone, which has been promoted in China. Its performance is better than that of Mag-spinel brick for most of the time. |
|
二、产品指标 II. product index |
产品名称 Product type |
|
硅莫砖 Alumisic |
硅莫砖 Alumisic |
硅莫砖 Alumisic |
|||
牌号 MRL BRAND |
|
CAS-168 |
CAS-165 |
CAS-155 |
|||
|
规格值 Standard V |
典型值 Typical V |
规格值 Standard V |
典型值 Typical V |
规格值 Standard V |
典型值 Typical V |
|
显气孔率A.P |
% |
19.0 |
18.5 |
20.0 |
19.0 |
21.0 |
20.0 |
体积密度B.D |
g/cm3 |
2.7 |
2.8 |
2.7 |
2.7 |
2.6 |
2.6 |
耐压强度 C.C.S |
Mpa |
100.0 |
110.0 |
100.0 |
110.0 |
80.0 |
90.0 |
荷重软化点R.U.L |
℃ (Ta) |
1650.0 |
1660.0 |
1600.0 |
1620.0 |
1500.0 |
1530.0 |
热震稳定性R.T.S |
950℃风冷/次 |
100次 |
>100次 |
100次 |
>100次 |
90次 |
>90次 |
热传导率T.C |
1000℃(W/Mk) |
1.3 |
1.3 |
1.3 |
1.3 |
1.4 |
1.4 |
化学成分 Chemical composition |
SC SiO2 |
30-33 |
33.0 |
25-30 |
29.5 |
20-25 |
25.0 |
Al2O3 |
65.0 |
67.0 |
63.0 |
65.0 |
60.0 |
62.0 |
|
用途 Applications
|
|
水泥窑下过渡带(窑口处) Low transition zone(outlet) |
水泥窑上过渡带 Upper transition zone |
水泥窑分解带和预热带及 预热器椎体部位 Decomposition zone, preheating zone and taper part of the preheater |
三、使用客户 III. Current customer |
|
|